The submission system is temporarily under maintenance. Please send your manuscripts to
Go to Editorial ManagerThe mechanical properties of low alloy steel are significantly influenced by retained austenite (RA). Consequently, using the X-Ray diffraction (XRD) measurement method, the retained Austenite volume fractions in AISI4330 alloy steel have been assessed in this article. The specimens underwent heat treatment at various heating temperatures (800 ֯ C, 900 ֯ C,1000 ֯ C) and cooling rates (Water and Oil). The findings demonstrate that retained Austenite formation rises with rising heating (Austenitizing) temperatures for the same quenching media as well as with rising cooling rates. The specimens were heated to a temperature of 1000 °C and then quenched in water, yielding the highest amount of retained austenite (7.733 wt%), and the lowest amount (1.977 wt%), which was obtained when the specimens were heated to a temperature of 800 °C and quenched in oil. The Vickers method was employed to conduct micro-hardness testing, and the results demonstrate that hardness values are reduced as heating temperatures increase. Optical microscopy was used to investigate the effects of retained austenite on the microstructure. The results show that bainite and/or martensite phases with a small amount of retained austenite dominate the microstructure at low cooling rates, whereas martensite and retained austenite phases dominate the microstructure at higher heating and cooling rates.
The present study aims to investigate the influence of heat treatment and surface finish on the behavior of crevice corrosion resistance of AISI 410 and 416 martensitic stainless steels thus, to quantify the conditions at which crevice corrosion minimize as possible. The experimental work carried out during this study involves material selection, chemical composition tests, specimens preparation before heat treatments, austenitizing at temperature range (925-1010˚C) and for holding time periods of (30, 45 and 90 min), air and oil quenching followed by tempering at heating range of (205- 605 ̊C) and for 45 min, micro hardness tests, specimens grinding, surface roughness measurements, crevice corrosion tests, crevice evaluation and microstructure tests. Theoretically, empirical equations for crevice maximum depth under the effect of surface roughness and hardness for both AISI 410 and 416 steels were determined. While for microstructure analysis, carbides average area was determined by using the ImageJ analysis program and a mathematical model was also predicted. Results showed that, as hardness and surface roughness increase crevice corrosion resistance decreases. Therefore, material treated by annealing can minimize crevice corrosion rates more than that treated with hardening.
Retained Austenite (RA) has great deal with the me- chanical properties of high strength low alloy steel. Therefore, in this paper, Retained Austenite volume fractions have been evaluated in AISI4340 alloy steel using two well-known meth- ods, X-Ray diffraction (XRD) and magnetic measurement methods. The specimens were heat treated using different heat- ing temperature and different cooling rate (different quenching media). A comparison between the results of two methods proved that there results were approximately Identical .The results show that Retained Austenite formation increase as heating (Austenizing ) temperature increase for the same quenching media ,as well as ,it increases by increasing cooling rate . The maximum amount of Retained Austenite found as (27.2 Wt %) which recognized when the specimens heated up to 1000˚C then quenched in Water while the minimum amount of Retained Austenite found as ( 7.06 wt%) when the specimens heated up to ( 800 ˚C) then quenched in Sand. Hardness tests using Vickers and Rockwell methods were used and the results show that hardness values decreased with increasing heating temperatures and the maximum Vickers micro-hardness and Rockwell hardness numbers were equal to (121.8HRB) and ( 516.35 HV) which were detected when heating up of the speci- mens were up to 800 ˚C then quenched in water. Tensile tests show that increasing cooling rate lead to increasing in Strength due to increasing of hardness which in turn, leads to increase in yielding points and ultimate strengths. Retained austenite effects on microstructure were investigated using scanning electron microscopy (SEM) and optical microscopy and the results show that at low cooling rate the microstructure consist of bainite and/or martensite phase with small amount of re- tained austenite, while, increasing heating temperature and cooling rate results in microstructure consist of martensite and retained austenite phases.
Friction stir processing is a new method of changing the properties of a metal through intense, localized plastic deformation ,this process mixes the material without changing the phase (by melting or otherwise) and creates a microstructure with fine, equiaxedgrains, It is used to improve the microstructural properties of metals. In this paper, the enhancement of mechanical propertiesof friction stir welding specimens at variable rotation speeds (1100, 1300 and 1500 rpm) with constant feed speed (60mm/min) for 6061-T6 aluminum alloy is studied by using the friction stir processing method at the same variable rotation speed and feed speed in order to transform a heterogeneous microstructure to a more homogeneous, refined microstructure. The best results of the welding line at the parameter 60 mm/min weld speed and 1300RPM rotation speed for the friction stir welding (FSW) and friction stir processing (FSP) where the efficiency reaches to 84.61% for FSW and 89.05% for FSP of the ultimate tensile strength of the parent metal.