Study of Failure of the Steam Tubes of Boiler Furnaces in Najebia Power Plant

Saleh E. Najim 1 Haider M. Mohammed 1
1 College of Engineering – Basrah University
History
  • Received: February 28, 2011
  • Available Online: May 31, 2011
DOI

https://doi.org/10.33971/bjes.11.1.6

Abstract

Failures in the steam tubes of boiler furnaces in Najebia power plant was studied experimentally. Visual examination, mechanical tests, microscopic test and chemical analyses were performed. Visual examination showed the types of failure in the tubes. Tensile and hardness tests were performed to estimate the variation in the mechanical properties of the tubes metal and compared with the new tubes. Microscopic test for the failed tubes used to recognize the difference in the microstructure to the metal of the tubes. Chemical analyses involved chemical composition of the tubes metal, river and feed water analyses, water treatment, fuel analyses and analysis of deposits and oxides on the external and internal sides. Overheating and wall thinning of the tubes resulted from oxygen escaping to the inner side of these tubes, and presence of deposits and oxides on the external and internal sides which led to failure was studied extensively. Engineering remedies were also given to confine the problem and to prevent it in future.

References

  1. Calannino J., “Prevent Boiler Tube Failure Part I : Fire-side Mechanisms”, Chemical Engg. Progress, pp33, 1993.
  2. Private Communications, "Najebia Power Plant", 1999.
  3. ASTM, “Tensile Testing of Metals”, Annual Book of ASTM Standards, E8, ASTM International, 2005.
  4. ASTM, “Specification for seamless carbon steel”, ASTM 106, 1995.
  5. ASTM, “Standard Test Methods for Rockwell Hardness of Metallic Materials”, Annual Book of ASTM Standards, E18, ASTM International, 2005.
  6. J. Horger, "Metals Engineering Design", ASME Hand Book, second edition, Mc Graw-Hill, 1965.
  7. K. Seymour Coburn, "Corrosion in Steam System", Metal Hand Book, V.1, 1961.
  8. ASM Committee on failure of pressure vessels, boilers and pressure piping, "Failure of Boilers and Related Steam Power Plant Equipment", American Society for Metals, V11, 2003.
  9. M.M.Nassrallah and V.K.Gouda, "Failure of boiler tubes in power plants", Br. Corrosion J., V.16, No.1, 1981.
  10. M.Islam and W.Riad, "Failure analysis of ruptured tubes from refinery steam boilers", Br. Corrosion J., V.24, No.1, 1989.
  11. M.G.Fontana and G. Mars, "Corrosion Engineering", 3rd, New York, Mc Graw-Hill, 1986.
  12. Metals Handbook, “Corrosion Fundamentals, Testing, and Protection”, Vol.13A, ASM, Metals Park, Ohio, 2003.
  13. R.W.Borio, "Coal ash deposition in boilers", Combustion Engineering Inc., Windsor, USA, 1986.